Polyurea AS 1044 (Anti-Static Polyurea)
AKFIX POLYUREA AS 1044 is a very fast curing, two component, aromatic, flexible, pure polyurea system coating derived from a reaction of an isocyanate prepolymer and an amine terminated resin blend. This product is especially applied to surfaces to build up antistatic coatings to avoid risks of ignition due to electrostatic charge. It can be applied to areas where flammable liquids of danger classes are stored. For protecting and coating purposes, this product can be applied on materials like concrete, metal, wood, ceramic and PU foam. The material must be applied utilizing high pressure, heated plural component spray proportioning equipment.
Properties
- Excellent flexibility
- Antistatic property
- Environmentally friendly
- Excellent thermal stability
- Excellent chemical resistance
- Excellent corrosion protection
- Excellent crack bridging properties
- 100% solid, VOC free, no solvents
- UV, chlorine and saltwater resistant
- Temperature and moisture insensitive
- Variable application thickness is possible
- Excellent impact and abrasion resistance
- Very good tensile and structural strength
- Fast reactivity and fast return to service time
- Excellent adhesion on concrete, steel, aluminum, plastics, fibers, wood, foam etc.
| S.Code | P.Code | Type | Volume | BoxQty | B.Pallet | Barcode |
| – | – | – | 200 kg | 1 | Barrel (Amine component) | – |
| – | – | – | 225 kg | 1 | Barrel (Iso component) | – |
- Laboratories
- Mining industry
- Transportation
- Oil and gas industry
- Hospitals and operating rooms
- Refineries and petrochemical industry
- Manufacturing facilities and storage areas
| Product Name | AKFIX POLYUREA AS 1044 | |||
| Component Properties | ||||
| Unit | Method | ISO COMPONENT (A( | ||
| Density (25°C) | gr/cm3 | ASTM D 1217 | 1,11±0,03 | 1,02±0,02 |
| Viscosity (25°C) | mPa.s | ASTM D 4878 | 700-800 | 300-600 |
| Shelf life | 9 months | 9 months | ||
| Process Properties | ||
| Unit | Datas | |
| Mix Ratio | By volume
By weight |
A=100 B=100
A= 112 B= 100 |
| Process temperature(°C) | °C | A:70-80 B: 70-80 |
| Process pressure (bar) | Bar | A: 150-200 B: 180-200 |
| %10 Sodium Chloride (NaCl) | Resistant |
| %10 Sulfuric Acid (H2SO4) | Resistant |
| %10 Hydrochloric Acid (HCl) | Resistant |
| %20 Phosphoric Acid (H3PO4) | Resistant |
| %20 Ammonium (NH4) + | Resistant |
| %50 Sodium hydroxide (NaOH) | Resistant |
| %20 Potassium hydroxide (KOH) | Resistant |
| Method | Datas | |
| Chemical structure | A: MDI Prepolymer
B: Amine Resin |
|
| Color | White, black, grey, yellow and any RAL color | |
| VOC content (%) | ASTM D1259 | 0 |
| Solid content (%) | ASTM D2697 | 100 |
| Gel time (sec) | 5-10 | |
| Tack free time (sec) | 15-30 | |
| Recoat time (hr) | 0-12 (without pretreatment) | |
| Post cure time (hr) | 24 | |
| Density (gr/cm3 ) | ASTM D792 | 0,99-1,03 |
| Tensile strength (MPa) | ASTM D638 | ≥ 16
|
| Modulus (MPa) | ASTM D638 | %100 elongation ≥10
%300 elongation ≥15 |
| Elongation at break (%) | ASTM D638 | ≥350 |
| Hardness (Shore D) | ASTM D2240 | 40-45 |
| Hardness (Shore A) | ASTM D2240 | 90-95 |
| Thermal Resistance | -25 °C-120°C | |
| Pull off strength (N/mm2 ) | ASTM D 4541 | Concrete: ≥2 Steel: ≥6 |
| Surface resistance(ohm) | DIN IEC 61340 | ≤0,5*109 |
| Reaction to Fire | EN 13501-1 | Class E |
| Co2 Permability | EN 1062-6 | SD = 76,45 m |
| Abrasion resistance | EN ISO 5470-1 | < 200 (H22, 1000 cycle) |
| Bond strength by pull-off | EN 1542 | 2,0 N/mm2 |
| Thermal Shock Resistance (200°C in 1 min. ) | Resistant | |
| Shelf Life | 9 months | |
| Consumption | 1,00- 1,1 kg/m2 /mm |