Akfix Polyurea HP 1044 (Abrasion Resistant Polyurea)
AKFIX POLYUREA HP 1044 is a very fast curing, two component, aromatic, pure polyurea system derived from a reaction of an isocyanate prepolymer and an amine terminated resin blend. It is a high performance product designed especially for industrial applications where high abrasion, chemical and corrosion resistance is a priority. For waterproofing and protecting purposes, this product can be applied on materials like concrete, metal, wood, ceramic and many other substrates. The material must be applied utilizing high pressure, heated plural component spray proportioning equipment.
Properties
- Seamless coating
- Broad color spectrum
- Environmentally friendly
- Excellent thermal stability
- Excellent chemical resistance
- Excellent corrosion protection
- 100% solid, VOC free, no solvents
- UV, chlorine and saltwater resistant
- Variable application thickness is possible
- Excellent impact and abrasion resistance
- Excellent impact and abrasion resistance
- Very good tensile and structural strength
- Fast reactivity and fast return to service time
- Excellent adhesion on concrete, steel, aluminum, plastics, fibers, wood, foam etc.
| S.Code | P.Code | Type | Volume | BoxQty | B.Pallet | Barcode |
| – | – | – | 200 kg | 1 | Barrel (Amine component) | – |
| – | – | – | 225 kg | 1 | Barrel (Iso component) | – |
General waterproofing and anticorrosion applications where high performance required as:
- Cargo containers
- Parking lots and garages
- Wastewater infrastructure
- Primary & secondary containments
- Power plants , refineries, oil and gas industry
- Cold storage facilities, loading docks and ramps
- Mining containment, process equipment and distribution
- Roads, bridge decks, railways, tunnels and truck bed liners
- Industrial & manufacturing facilities, storage, load and high traffic areas
| Product Name | AKFIX POLYUREA HP 1044 (ABRASION RESISTANT) | |||
| Component Properties | ||||
| Unit | Method | ISO COMPONENT (A) | AMINE COMPONENT (B) | |
| Density (25°C) | gr/cm3 | ASTM D 1217 | 1,11±0,03 | 1,02±0,02 |
| Viscosity (25°C) | mPa.s | ASTM D 4878 | 700-800 | 300-600 |
| Shelf life | 9 months | 9 months | ||
| Process Properties | ||
| Unit | Datas | |
| Mix Ratio | By volume
By weight |
A=100 B=100
A= 112 B= 100 |
| Process temperature(°C) | °C | A:70-80 B: 70-80 |
| Process pressure (bar( | Bar | A: 180-200 B: 180-200 |
| Method | Datas | |
| Chemical structure | A: MDI Prepolymer
B: Amine Resin |
|
| VOC content (%) | ASTM D1259 | 0 |
| Solid content (%) | ASTM D2697 | 100 |
| Gel time (sec) | 3-5 | |
| Tack free time (sec) | 10-25 | |
| Recoat time (hr) | 0-12 (without pretreatment) | |
| Post cure time (hr) | 24 | |
| Density (gr/cm3 ) | ASTM D792 | 0,99-1,03 |
| Tensile strength (MPa) | ASTM D638 | ≥ 20 |
| Elongation at break (%) | ASTM D638 | ≥200 |
| Hardness (Shore D) | ASTM D2240 | 50-45 |
| Tear strength (N/mm) | ASTM D 624 | ≥50 |
| Taber abrasion (mg) | EN ISO 5470-1 | ˂25 (H22, 1000 cycle) |
| Impact resistance | EN ISO 6272-1 | Class III |
| Thermal Resistance | -30 °C-100°C | |
| Pull off strength (N/mm2 ) | ASTM D 4541 | Concrete: ≥2,5 Steel: ≥6 |