Akfix Polyurea AL 1070 (Aliphatic)
Akfix Polyurea AL 1070 is a %100 solid, fast curing, 2 component, UV resistive, aliphatic pure polyurea system. Its formulation is designed for maintaining high color stability and preventing discoloration where surfaces are exposed to sun light continuously. While it can be directly used on most surfaces, it also can be used as a top layer on epoxy, polyurethane and polyurea. After fully cured, it forms a coating material with high tensile strength and abrasion resistance. For protection and coating purposes, it can be applied on concrete, metal, wood, ceramic and PU foam. It can form strong films in wide variety of thicknesses. The material must be applied utilizing high pressure, heated plural component spray proportioning equipment.
Properties
- Anticorrosive
- %100 color stability
- Broad color spectrum
- High Hydrolysis resistance
- %100 solid, VOC free, no odor
- Excellent temperature stability
- Excellent resistance to UV light
- Variable application thickness is possible
- Very good tensile and structural strength
- No sensitivity to temperature and humidity
- Fast reactivity and fast return to service time
- Seamless and joint-less coating with high water resistance
- Excellent adhesion on concrete, steel, aluminum, plastics, wood, etc.
| S.Code | P.Code | Type | Volume | BoxQty | B.Pallet | Barcode |
| WPAL1070.2005 | POLYUREA AL1070 | RAL 7040 | 410 kg set (210+200kg) | 1 | – | – |
| WPAL1070.2009 | POLYUREA AL1070 | RAL 5012 | 410 kg set (210+200kg) | 1 | – | – |
| WPAL1070.2010 | POLYUREA AL1070 | RAL 3000 | 410 kg set (210+200kg) | 1 | – | – |
- Furniture industry
- Decorative designs
- Wind energy plants
- Airports, shipyards and marina
- Swimming pools and water parks
- Roofs, garages and parking lots
- Amusement parks and playgrounds
- At exterior coatings where color stability is required
| Product Name | AKFIX POLYUREA AL 1070 (ALIPHATIC) | |||
| Component Properties | ||||
| Unit | Method | MDI Prepolymer (A) | Amine Resin (B) | |
| Density (25°C) | gr/cm3 | ASTM D 1217 | 1,11±0,03 | 1,02±0,02 |
| Viscosity (25°C) | mPa.s | ASTM D 4878 | 700-800 | 300-600 |
| Shelf life | 9 months | 9 months | ||
| Process Properties | ||
| Unit | Datas | |
| Mix Ratio | By volume
By weight |
A=100 B=100
A= 112 B= 100 |
| Process temperature(°C) | °C | A:70-80 B: 70-80 |
| Process pressure (bar( | Bar | A: 150-200 B: 150-200 |
| Method | Datas | |
| Chemical structure | A: MDI Prepolymer
B: Amine Resin |
|
| VOC content (%) | ASTM D1259 | 0 |
| Solid content (%) | ASTM D2697 | 100 |
| Gel time (sec) | 15-30 | |
| Tack free time (sec) | 45-60 | |
| Recoat time (hr) | 0-12 | |
| Density (gr/cm3 ) | ASTM D792 | 1,05-1,08 |
| Tensile strength (MPa) | ASTM D638 | >16 |
| Elongation at break (%) | ASTM D638 | ≥400 |
| Hardness (Shore D) | ASTM D2240 | 40-45 |
| Abrasion resistance (mg) | < 33 (H22, 1000 cycle) | |
| Pull off strength (N/mm2 ) | ASTM D 4541 | Concrete: ≥2,5 Steel: ≥6 |