Akfix Polyurea 1045 (Eco Pure)
AKFIX Polyurea 1045 is a very fast set, rapid curing, flexible, two component, aromatic pure polyurea coating system derived from a reaction of an isocyanate prepolymer and an amine terminated resin blend. The system is designed as a waterproofing and floor protective coating for concrete, metal, wood, ceramic, geotextile and PU foam substrates. The material must be applied utilizing high pressure, heated plural component spray proportioning equipment.
Properties
- Seamless coating
- Excellent flexibility
- Broad color spectrum
- Excellent thermal stability
- Excellent chemical resistance
- 100 %solid, VOC free, no odor
- UV, chlorine and saltwater resistant
- Variable application thickness possible
- Temperature and moisture insensitive
- Excellent impact and abrasion resistance
- Very good tensile and structural strength
- Fast reactivity and fast return to service time
- Excellent adhesion on concrete, steel, aluminum, plastics, fibers, wood, foam etc.
S.Code | P.Code | Type | Volume | BoxQty | B.Pallet | Barcode |
– | – | – | 200 kg | 1 | Barrel (Amine component) | – |
– | – | – | 225 kg | 1 | Barrel (Iso component) | – |
- Floors– industrial floors, hospitals, factories
- Construction– roads, bridge decks, airports, line striping.
- Marine industry– ship’s underwater part and ship’s decks protection and ship docks
- On thermal insulation products for waterproofing (polyurethane foam, EPS, XPS etc.)
- Leisure industry– water parks, aquariums linings, playgrounds and decorative applications
- General waterproofing and anticorrosion applications– tanks, pools, swimming pools, ponds, pipes, pipelines, waste water treatments, manholes and sewer linings, roof, balcony and terrace coatings.
Product Name | AKFIX POLYUREA 1045 (ECO PURE) | |||
Component Properties | ||||
Unit | Method | ISO COMPONENT (A) | AMINE COMPONENT (B) | |
Density (25°C) | gr/cm3 | ASTM D 1217 | 1,11±0,03 | 1,02±0,02 |
Viscosity (25°C) | mPa.s | ASTM D 4878 | 700-800 | 300-600 |
Shelf life | 9 months | 9 months |
Process Properties | ||
Unit | Datas | |
Mix Ratio | By volume
By weight |
A=100 B=100
A= 112 B= 100 |
Process temperature(°C) | °C | A:70-80 B: 70-80 |
Process pressure (bar( | Bar | A: 180-200 B: 180-200 |
METHOD | DATAS | |
Chemical structure | A: MDI Prepolymer B: Amine Resin | |
VOC content (%) | ASTM D1259 | 0 |
Solid content (%) | ASTM D2697 | 100 |
Gel time (sec) | 5-10 | |
Tack free time (sec) | 15-30 | |
Recoat time (hr) | 0-12 (without pretreatment) | |
Post cure time (hr) | 24 | |
Density (gr/cm3 ) | ASTM D792 | 0,99-1,03 |
Tensile strength (MPa) | ASTM D638 | ≥ 15 |
Modulus (MPa) | ASTM D638 | %100 elongation ≥10
%300 elongation ≥12 |
Elongation at break (%) | ASTM D638 | ≥375 |
Hardness (Shore D) | ASTM D2240 | 35-40 |
Hardness (Shore A) | ASTM D2240 | 90-95 |
Tear strength (N/mm) | ASTM D 624 | ≥40 |
Taber abrasion (mg) | EN ISO 5470-1 | ˂100 (H22/1000 cycle) |
Impact resistance | EN ISO 6272-1 | Class III |
Thermal Resistance | -30 °C-100°C | |
Pull off strength (N/mm2 ) | ASTM D 4541 | Concrete: ≥2,5 Steel: ≥6 |