Akfix 610 PU Express Montage Adhesive (Transparent)
Akfix 610 is a single component, fast curing polyurethane based adhesive. It combines high bond strength with fast curing. The water resistance property makes it exceptionally good at bonding wooden surfaces where water splash and moisture is an issue.
Properties
- Low odor.
- Transparent.
- Non-shrinking.
- Good filling properties.
- Fast curing, low press time.
- Low consumption, economical.
- Usable on slightly wet substrates.
- Very good resistance to chemicals.
- Very good resistance to chemicals.
- Conforms to D4 according to DIN EN 204.
- Thixotropic, non-sag, ideal for vertical joints.
- Extremely high bond strength on wooden substrates.
- Excellent resistance to moisture and weather conditions.
| S.Code | P.Code | Type | Volume | BoxQty | B.Pallet | Barcode |
| GA400 | 610 | Aluminum Cartridge | 310 | 12 | – | – |
| GA400P | 610 | Plastic Cartridge | 310 ml | 12 | – | – |
| GA305 | 610 | Aluminum Tube | 50 ml | 30 | – | – |
- It is suitable for use in construction and repair applications where a permanent strong bond is required between porous-porous and porous nonporous surfaces.
- Bonding wooden surfaces at bathroom, kitchens, decks etc. where there is a constant moisture and water contact risk.
- It can be used for bonding various kinds of construction materials such as wood, MDF, concrete, metal, polystyrene and polyurethane foam, marble, granite and ceramic etc.
| Product Name | 610 PU EXPRESS MONTAGE ADHESIVE | |
| Basis | Polyurethane prepolymer | |
| Color | Transparent | |
| Density | 1.13 ± 0.03 gr/ml | |
| Tack-Free Time | 5 – 10 min. (at 23°C and %50 R.H.) | |
| Consistency | Thixotropic | |
| Consumption | Approx. 150 g/m2 | |
| Shrinkage | None | |
| Pressing Time | 15 – 20 min.* | |
| Temperature Resistance | -20o C to +80 o C | |
| Application Temperature | +5 o C to +35 o C | |
| Maximum Shear Strength (beech-beech) | ||
| After 15 min | > 50 kgf/cm2 | |
| After 24 hours | > 100 kgf/cm2 | |
| After 7 days | ≈ 120 kgf/cm2 | (DIN EN 205) |
| After 7 days at 80 ˚C | ≈ 100 kgf/cm2 | (WATT 91) |