Akfix Polyurea PA 1005 Polyaspartic Hard
Two component, rapid curing, UV resistant, excellent color stable new generation polyaspartic based polyurea surface coating system for both decorative and protective applications. On account of the UV and color fast properties, it is ideal for use as thin layer coating and clear topcoat sealer for surface protection on existing coating systems. After the product is completely cured, it forms a glossy, smooth top layer with high scratch, abrasion and chemical resistance. Polyaspartic system can be applied in a single or multiple coats by roll, brush or squeegee to a variety of substrates including concrete and metal.
Properties
- Perfect thermal stability
- High hydrolysis resistance
- Long working and gel time
- Excellent UV light resistance
- Excellent chemical resistance
- Easy application and spreading
- Resistant to chlorine and saltwater
- Excellent color stability and gloss retention
- High abrasion, impact and corrosion resistance
- Available in transparent and several RAL colors
- Excellent adhesion to concrete and metal substrates
- Rapid return to service (return to service in 24 hours)
- Fast reactivity and cure time (applicable to pedestrian traffic after 3-4 hours)
| S.Code | P.Code | Type | Volume | BoxQty | B.Pallet | Barcode |
| WPPA05206 | – | RAL 7040 | 10kg (6kg+4 kg) | 1 | – | – |
| WPPA05200 | – | RAL 5012 | 10kg (6kg+4 kg) | 1 | – | – |
| WPPA05209 | – | RAL 3000 | 10kg (6kg+4 kg) | 1 | – | – |
| WPPA05205 | – | Transparent | 10kg (6kg+4 kg) | 1 | – | – |
- Deck coatings
- Aircraft hangers
- Wind energy plants
- Restaurant and hospital flooring
- Industrial and commercial flooring
- Swimming pools, terraces and garage floors
- Clear sealer over decorative concrete surfaces
- Water parks, amusement parks and decorative applications
- As top layer over polyurea coatings where UV resistance and color stability is required
| Product Name | KFIX POLYUREA PA 1005 (POLYASPARTIC) | |||
| Component Properties | ||||
| Unit | Method | MDI Prepolymer (A) | Amine Resin (B) | |
| Density (25°C) | gr/cm3 | ASTM D 1217 | 1,07-1,1 | 1,15-1,17 |
| Viscosity (25°C) | mPa.s | ASTM D 4878 | 1000-1100 | 720-750 |
| Shelf life | 9 months | 9 months | ||
| Method | Datas | |
| Chemical structure | A: Amine Resin
B:HDI Prepolymer |
|
| Mix ratio (by weight) | 60:40 (A:B) | |
| Consumption (g/m2 ) | 150-200 | |
| Recommended thickness (µm) | 150-200 | |
| VOC content (%) | ASTM D1259 | 0 |
| Solid content (%) | ASTM D2697 | 95 |
| Gel time (min) | 30-35* | |
| Tack free time (min) | 50-60* | |
| Pedestrian traffic time (hr) | 3-4* | |
| Full cure time (day) | 7* | |
| Min. recoat time (hr) | 2* | |
| Max. recoat time (hr) | 24* | |
| Tensile strength (MPa) | ASTM D638 | 4-6 |
| Elongation at break (%) | ASTM D638 | >30 |
| Hardness (Shore D) | ASTM D2240 | 65-70 |
| Abrasion resistance (mg) | EN ISO 5470-1 | < 15 (H22, 1000 cycle) |