Akfix Polyurea HB 1010 (Hybrid Systems)
AKFIX POLYUREA HB 1010 is a very fast set, rapid curing, flexible, two component hybrid polyurea system. It is derived from a reaction of an isocyanate prepolymer and an amine terminated resin blend. It can be applied as an economic waterproofing and coating alternative to pure polyurea products. The material must be applied utilizing high pressure, heated plural component spray proportioning equipment. Polyurea HB 1010 conforms to requirements of the EN 1504-2 standard (concrete surface protection systems).
Properties
- Seamless coating
- Excellent flexibility
- Broad color spectrum
- Environmentally friendly
- Excellent crack bridging properties
- 100% solid, VOC free, no solvents
- Variable application thickness possible
- Very good tensile and structural strength
- Fast reactivity and return to service time
- Economic alternative to pure polyurea products
- Excellent adhesion on concrete, steel, aluminum, plastics, fibers, wood, foam etc.
| S.Code | P.Code | Type | Volume | BoxQty | B.Pallet | Barcode |
| – | – | – | 200 kg | 1 | Barrel (Amine component) | – |
| – | – | – | 225 kg | 1 | Barrel (Iso component) | – |
- Play grounds and decorative applications
- Waterproofing of ground concrete and load bearing walls
- On thermal insulation products for waterproofing (polyurethane foam, EPS, XPS etc.)
- General waterproofing under ceramic, screed concrete, marble and other floor coverings
- General waterproofing for light foot traffic areas like roofs, balconies, terraces, walkways and public area.
| Product Name | AKFIX POLYUREA HB 1010 (HYBRID) | |||
| Component Properties | ||||
| Unit | Method | MDI Prepolymer (A) | Amine Resin (B) | |
| Density (25°C) | gr/cm3 | ASTM D 1217 | 1,11±0,03 | 1,02±0,02 |
| Viscosity (25°C) | mPa.s | ASTM D 4878 | 700-800 | 300-600 |
| Shelf life | 9 months | 9 months | ||
| Process Properties | ||
| Unit | Datas | |
| Mix Ratio | By volume
By weight |
A=100 B=100
A= 112 B= 100 |
| Process temperature(°C) | °C | A:70-80 B: 70-80 |
| Process pressure (bar( | Bar | A: 180-200 B: 180-200 |
| Method | Datas | |
| Chemical structure | A: MDI Prepolymer
B: Amine Resin |
|
| VOC content (%) | ASTM D1259 | 0 |
| Solid content (%) | ASTM D2697 | 100 |
| Gel time (sec) | 5-10 | |
| Tack free time (sec) | 15-30 | |
| Recoat time (hr) | 0-12(without any pretreatment) | |
| Density (gr/cm3 ) | ASTM D792 | 0,99-1,03 |
| Tensile strength (MPa) | ASTM D638 | ≥15 |
| Modulus (MPa) | ASTM D638 | %100 elongation ≥ 5 |
| Elongation at break (%) | ASTM D638 | ≥350 |
| Hardness (Shore A) | ASTM D2240 | 90-95 |
| Tear strength (N/mm) | ASTM D-624 | ≥25 |
| Taber abrasion (mg) | EN ISO 5470-1 | ˂250 (H22, 1000 cycle) |
| Impact resistance | EN ISO 6272-1 | Class III |
| Pull off strength (N/mm2 ) | ASTM D4541 | Concrete: ≥3 Steel: ≥6 |