Akfix Polyurea FX 1044 (Enhanced Flexibility)
Akfix POLYUREA FX 1044 is a very fast curing, two component and elastomeric pure polyurea system. In addition to having basic properties of polyurea systems properties, it has a lot more elasticity to be able to use where elasticity is essential like in metal roof and geotextile coatings. It can be used with confidence in both interior and exterior applications. The material must be applied utilizing high pressure, heated plural component spray proportioning equipment.
Properties
- Seamless coating
- Excellent flexibility
- Broad color spectrum
- Environmentally friendly
- Excellent flexibility and elongation
- Excellent crack bridging properties
- 100% solid, VOC free, no solvents
- UV, chlorine and saltwater resistant
- Temperature and moisture insensitive
- Variable application thickness is possible
- Very good tensile and structural strength
- Fast reactivity and fast return to service time
- Excellent adhesion on concrete, steel, aluminum, plastics, fibers, wood, foam etc.
| S.Code | P.Code | Type | Volume | BoxQty | B.Pallet | Barcode |
| – | – | – | 200 kg | 1 | Barrel (Amine component) | – |
| – | – | – | 225 kg | 1 | Barrel (Iso component) | – |
General waterproofing applications where high flexibility necessary as:
- Geotextile coating
- Decorative applications
- Pools and storage tanks
- Water and amusement parks
- Roofs, terraces and garages
| Product Name | AKFIX POLYUREA FX 1044 (ENHANCED FLEXIBILITY) | |||
| Component Properties | ||||
| Unit | Method | ISO COMPONENT (A) | AMINE COMPONENT (B) | |
| Density (25°C) | gr/cm3 | ASTM D 1217 | 1,11±0,03 | 1,02±0,02 |
| Viscosity (25°C) | mPa.s | ASTM D 4878 | 700-800 | 300-600 |
| Shelf life | 9 months | 9 months | ||
| Process Properties | ||
| Unit | Datas | |
| Mix Ratio | By volume
By weight |
A=100 B=100
A= 112 B= 100 |
| Process temperature(°C) | °C | A:70-80 B: 70-80 |
| Process pressure (bar) | Bar | A: 180-200 B: 180-200 |
| Method | Datas | |
| Chemical structure | A: MDI Prepolymer
B: Amine Resin |
|
| VOC content (%) | ASTM D1259 | 0 |
| Solid content (%) | ASTM D2697 | 100 |
| Gel time (sec) | 20-30 | |
| Tack free time (sec) | 60-90 | |
| Recoat time (hr) | 0-12 (without pretreatment) | |
| Post cure time (hr) | 24 | |
| Density (gr/cm3 ) | ASTM D792 | 0,99-1,03 |
| Tensile strength (MPa) | ASTM D638 | ≥ 10 |
| Modulus (MPa) | ASTM D638 | %100 elongation ≥3
%300 elongation ≥5 |
| Elongation at break (%) | ASTM D638 | ≥500 |
| Hardness (Shore A) | ASTM D2240 | 70-75 |
| Pull off strength (N/mm2 ) | ASTM D 4541 | oncrete: ≥2,5 Steel: ≥6 |